MXD6 Polyadipyl-m-benzoylamine, referred to as mxd6, generally referred to as "nylon mxd6", resin than other engineering plastics have higher mechanical strength and modulus, is also a special high barrier nylon material. Although the barrier of mxd6 is slightly worse than that of pvdc and evoh, its barrier is not affected by temperature and humidity, which is especially suitable for high temperature and humid occasions. In today's barrier packaging and plastic instead of steel general trend, nylon mxd6 has become one of the most eye-catching new plastic varieties. Structure performance: PA MXD6 nylon material has high strength, high rigidity, high thermal deformation temperature, small thermal expansion coefficient; Dimensional stability, low water absorption rate and small size change after water absorption, mechanical strength changes less; Forming shrinkage is small, suitable for precision forming processing; Excellent coating performance, especially suitable for high temperature surface coating; Excellent barrier to oxygen, carbon dioxide and other gases. Excellent mechanical and thermal properties and high strength, high modulus and heat resistance, high barrier, excellent cooking resistance Advantages 1、Maintain high strength and rigidity in a wide temperature range 2、High heat deflection temperature, small coefficient of thermal expansion 3、Low water absorption, small size change after water absorption, less mechanical strength reduction 4、Small shrinkage rate of molding, suitable for precision molding process 5、Excellent paintability, especially suitable for surface painting under high temperature 6、Excellent barrier to oxygen, carbon dioxide and other gases MXD6-LGF MXD6 applications in the plastics modification industry MXD6 can be compounded with glass fibers, carbon fibers, minerals and/or advanced fillers for materials containing 50-60% glass fiber reinforcement with exceptional strength and stiffness. Even when filled with high levels of glass fiber, its smooth, resin-rich surface creates a high gloss finish like no glass fiber, making it ideal for painting, metal coating or creating naturally reflective housings. 1、High fluidity for thin wall It is a very high flowing resin that can easily fill thin walls as thin as 0.5 mm thick even with glass fiber content as high as 60%. 2、Excellent surface finish The resin-rich perfect surface has a highly polished appearance, even with a high glass fiber content. 3、Very high strength and stiffness MXD6 with 50-60% glass fiber reinforcement has a tensile and flexural strength similar to many cast metals and alloys. 4、Good dimensional stability At ambient temperature, the coefficient of linear expansion (CLTE) of MXD6 glass fiber composite is similar to that of many cast metals and alloys. It is highly reproducible due to low shrinkage and the ability to maintain tight tolerances (length tolerances can be as low as ± 0.05% if properly formed). TDS for reference only Application MXD6 replaces metal to make high quality structural parts for automobiles, electronics and electrical appliances 自動車部品では機械的強度が高く、耐油性に優れ、120～160℃の範囲で長時間使用できる材料製品が求められる場面が多くあります。ガラス繊維強化MXD6は、225℃までの耐熱性と高温下での強度保持率が高く、自動車エンジンのシリンダーブロック、シリンダーヘッド、ピストン、シンクロギヤ等に使用されています。MXD6/PPOアロイは、高温耐性、高強度、耐油性、耐摩耗性、寸法安定性などの特性を備えており、自動車ボディの垂直外板、前後フェンダー、ホイールカバーなどに使用でき、プレス成形ではほとんど不可能です。鋼板。自動車の湾曲部分やシャーシ。 私たちに関しては

ABS ABS resin is a thermoplastic polymeric structural material with high strength, good toughness and easy processing and molding. Long glass fiber reinforced ABS granules Long glass fiber reinforced plastic is based on the original pure plastic, adding long glass fiber and other additives, so as to improve the scope of use of the material. Generally speaking, most of the long glass fiber reinforced materials are mostly used in the structural parts of products, which is a structural engineering material, such as PP, ABS, PA66, PA6, PBT, PPS, etc. Advantages After long glass fiber reinforced,  long glass fiber is a high temperature resistant material, therefore, the heat resistance temperature of reinforced plastics is much higher than before without long glass fiber. After long glass fiber reinforced, the addition of long glass fiber restricts the movement of polymer chains between plastics, so the shrinkage of reinforced plastics is much lower and the rigidity is much higher. After long glass fiber reinforcement, the reinforced plastic will not be stress cracked, and the impact resistance of the plastic will be improved. After long glass fiber reinforcement, long glass fiber is a high-strength material, which also greatly improves the strength of plastic, such as: tensile strength, compression strength, bending strength, much higher. After the long glass fiber reinforcement, the burning performance of the reinforced plastic decreases a lot due to the addition of long glass fiber and other additives, and most of the materials cannot be ignited, which is a kind of flame retardant material. Datasheet for reference Application Can be used at many fields. For more details, please contact us. Other products you may wonder                                                                                                                                                                               PP-NA-LGF                              PA6-NA-LGF                           TPU-NA-LGF                     Frequently asked questions Q. What are the differences and advantages of long fiber materials and thermosets and staple fibers? A. Compared with the short fiber, it has more excellent performance in mechanical properties. It is more suitable for large products and structural parts. It has 1-3 times higher toughness than short fiber, and the tensile strength (strength and rigidity) is increased by 0.5-1 times. Compared with thermosets, it is more environmentally friendly. It can be recycled and reused,  and has simple molding efficiency, lower cost etc. But its mechanical properties are worse than thermosets. Q. Using a long fiber reinforced thermoplastic material, will it block the die hole due to the long length of the fiber or not? A. ガラス長繊維やカーボン長繊維を使用する場合、LFT-Gに適しているかどうかを評価する必要があります。製品が小さすぎる場合、または塗布が長繊維材料に適していない場合。長繊維自体が金型ノズルに必要な要件を備えています。 Q. 長繊維強化熱可塑性材料を使用する場合、補強方法と材料の長さはどのように選択すればよいですか? A. 材料の選択は製品の要件によって異なります。製品の要求性能に応じて、内容物をどの程度強化するか、どの程度の長さが適切であるかを判断する必要があります。 アモイLFT複合プラスチック有限公司 ご提供させていただきます 1. LFTおよびLFRT材料の技術パラメータと最先端の設計 2. 金型正面の設計と推奨事項 3. 射出成形、押出成形等の技術サポートの提供

MXD6プラスチック | 長ガラス繊維強化MXD6（MXD6-LGF） MXD6とは何ですか？ ポリアジピル-m-ベンゾイルアミン、通称 MXD6 または ナイロンMXD6 MXD6は、高性能エンジニアリングプラスチックです。他のエンジニアリングプラスチックと比較して、MXD6は高い機械的強度と弾性率を誇ります。また、特殊な高バリア性ナイロンで、酸素と二酸化炭素に対する耐性に優れています。PVDCやEVOHとは異なり、温度や湿度の影響を受けないため、高温多湿の環境に最適です。 構造および機械性能 MXD6ナイロンは、高強度、高剛性、高い熱変形温度、低熱膨張、優れた寸法安定性、そして低吸水性を特徴としています。吸水後も機械的特性の変化は最小限に抑えられています。MXD6は、精密成形に適した低収縮性、高温下での優れた塗装性、そして優れたバリア性を備えています。 MXD6の利点 広い温度範囲にわたって高い強度と剛性を維持 高い熱変形温度と低い熱膨張係数 吸水性が低く、機械的特性の低下が最小限 成形収縮が小さく、精密成形工程に適しています 特に高温下でも優れた塗装性 酸素、二酸化炭素、その他のガスに対する優れたバリア MXD6-LGF | 長ガラス繊維強化MXD6 MXD6は、長ガラス繊維、炭素繊維、鉱物、高度な充填剤と混合することで、50～60%のガラス繊維強化複合材を製造できます。これにより、塗装、金属コーティング、反射ハウジングなどに最適な、滑らかで樹脂を豊富に含んだ表面を維持しながら、卓越した強度と剛性が得られます。 MXD6-LGFの主な利点 薄壁でも高い流動性： ガラス繊維含有量が 60% でも、0.5 mm の薄壁を充填できます。 優れた表面仕上げ： 樹脂を豊富に含む表面は、繊維含有量が多いにもかかわらず、光沢のある外観を実現します。 非常に高い強度と剛性： ガラス繊維を 50 ～ 60% 含む多くの鋳造金属や合金に匹敵します。 優れた寸法安定性： 収縮率が低く、許容誤差が小さく、線膨張係数は多くの金属と同様です。 MXD6-LGF TDS（技術データシート） MXD6-LGFの用途 MXD6-LGF 自動車、電子機器、電気機器などの高品質構造部品において、金属の代替として使用できます。高い機械的強度と耐油性が求められる環境下でも優れた性能を発揮し、120～160℃の高温環境下で長期間動作します。ガラス繊維強化により、MXD6は225℃までの耐熱性を維持します。自動車エンジンのシリンダーブロック、シリンダーヘッド、ピストン、同期ギアなどに最適です。 MXD6/PPO 合金は、耐熱性、強度、耐摩耗性、耐油性、寸法安定性に優れているため、自動車のボディパネル、フェンダー、ホイールカバー、複雑な曲面部品の金属代替を可能にします。 私たちについて