PA6 ポリアミド 6 長ガラス繊維コンパウンド電子機器電動工具用の高靭性

PA6-LGF

PA6改質プラスチックは、純粋なPA6スライスをマトリックスとし、ブレンド、充填、強化、共重合、架橋などの方法によって内部および外部の特性を改善し、PA6の応用分野の約15％を占めています。

ガラス長繊維の含有量は20%〜60%であり、ガラス長繊維の含有量はさまざまな製品特性に応じて制御されます。高強度、優れた耐熱性、耐衝撃性があり、一部の金属材料の軽量化を代替することができます。電動工具のシェル、園芸工具、歯車、スポーツ用品、自動車部品などに広く使用されています。

PA6-LGFのその他の仕様

難燃性PA6

PA6 material has poor flame retardant performance and belongs to flammable materials, but flame retardants can change the combustion characteristics of polymers. Through mechanical mixing method, flame retardants are added to the master material to change the flammable characteristics. The products are divided into: nitrogen flame retardants, phosphorus flame retardants, environmental protection bromine flame retardants, mineral filled flame retardants, which can be used in switches, low-voltage electrical housing, wiring terminals, circuit breakers, etc.

Toughen PA6

Mixed with an appropriate amount of toughening agent, the product has the characteristics of low temperature resistance, high flexibility, high fluidity, low shrinkage, low water absorption, high impact resistance, aging resistance and so on. It can be used for baby carriage parts, rolling belts, line clips, connectors and so on.

Application

In addition to the above applications, in high-end fields such as rail transit, medical treatment, military industry and aerospace, nylon 6 modified plastics are used more and more widely, and PA6 modified plastics are used everywhere in daily life.

TDS for reference

Nylon reinforced material is made of PA6/PA66 resin as the base material and adding a certain proportion of glass fiber modification. Because nylon itself is not strong enough, by adding 20 to 60 percent of the fiber, to increase its strength. In particular, 30% strength is considered the most appropriate ratio. Also added to 40-50%, according to the specific requirements of different products, coupled with the appropriate formula, can be successful.

Advantage of Long glass fiber compounds

1. After glass fiber reinforcement, glass fiber is a high temperature resistant material, therefore, the heat resistance temperature of reinforced plastics is much higher than before without glass fiber, especially nylon plastics;

2. After glass fiber reinforcement, due to the addition of glass fiber, limited the mutual movement between polymer chains of plastics, therefore, the shrinkage rate of reinforced plastics decreases a lot, rigidity is greatly improved;

3. After glass fiber reinforcement, the reinforced plastic will not stress crack, at the same time, the anti-impact performance of plastic is improved a lot;

4. After glass fiber reinforcement, glass fiber is a high strength material, which also greatly improves the strength of plastic, such as: tensile strength, compression strength, bending strength, improve a lot;

5. glass fiber reinforced after, due to the addition of glass fiber and other additives, the combustion performance of reinforced plastics decreased a lot, most of the material can not ignite, is a kind of flame retardant material.

Xiamen LFT composite plastic Co., Ltd.

アモイ LFT 複合プラスチック有限公司は、LFT&LFRT に焦点を当てたブランド企業です。長ガラス繊維シリーズ (LGF) および長炭素繊維シリーズ (LCF)。同社の熱可塑性LFTはLFT-D成形にも使用できます。お客様のご要望に合わせて製作可能です:長さ5~25mm。同社の長繊維連続浸透強化熱可塑性プラスチックは ISO9001&16949 システム認証に合格しており、製品は多くの国内商標と特許を取得しています。