PA6-LGF PA6改質プラスチックは、純粋なPA6スライスをマトリックスとし、ブレンド、充填、強化、共重合、架橋などの方法によって内部および外部の特性を改善し、PA6の応用分野の約15％を占めています。 ガラス長繊維の含有量は20%〜60%であり、ガラス長繊維の含有量はさまざまな製品特性に応じて制御されます。高強度、優れた耐熱性、耐衝撃性があり、一部の金属材料の軽量化を代替することができます。電動工具のシェル、園芸工具、歯車、スポーツ用品、自動車部品などに広く使用されています。 PA6-LGFのその他の仕様 難燃性PA6 PA6 material has poor flame retardant performance and belongs to flammable materials, but flame retardants can change the combustion characteristics of polymers. Through mechanical mixing method, flame retardants are added to the master material to change the flammable characteristics. The products are divided into: nitrogen flame retardants, phosphorus flame retardants, environmental protection bromine flame retardants, mineral filled flame retardants, which can be used in switches, low-voltage electrical housing, wiring terminals, circuit breakers, etc. Toughen PA6 Mixed with an appropriate amount of toughening agent, the product has the characteristics of low temperature resistance, high flexibility, high fluidity, low shrinkage, low water absorption, high impact resistance, aging resistance and so on. It can be used for baby carriage parts, rolling belts, line clips, connectors and so on. Application In addition to the above applications, in high-end fields such as rail transit, medical treatment, military industry and aerospace, nylon 6 modified plastics are used more and more widely, and PA6 modified plastics are used everywhere in daily life. TDS for reference Nylon reinforced material is made of PA6/PA66 resin as the base material and adding a certain proportion of glass fiber modification. Because nylon itself is not strong enough, by adding 20 to 60 percent of the fiber, to increase its strength. In particular, 30% strength is considered the most appropriate ratio. Also added to 40-50%, according to the specific requirements of different products, coupled with the appropriate formula, can be successful. Advantage of Long glass fiber compounds 1. After glass fiber reinforcement, glass fiber is a high temperature resistant material, therefore, the heat resistance temperature of reinforced plastics is much higher than before without glass fiber, especially nylon plastics; 2. After glass fiber reinforcement, due to the addition of glass fiber, limited the mutual movement between polymer chains of plastics, therefore, the shrinkage rate of reinforced plastics decreases a lot, rigidity is greatly improved; 3. After glass fiber reinforcement, the reinforced plastic will not stress crack, at the same time, the anti-impact performance of plastic is improved a lot; 4. After glass fiber reinforcement, glass fiber is a high strength material, which also greatly improves the strength of plastic, such as: tensile strength, compression strength, bending strength, improve a lot; 5. glass fiber reinforced after, due to the addition of glass fiber and other additives, the combustion performance of reinforced plastics decreased a lot, most of the material can not ignite, is a kind of flame retardant material. Xiamen LFT composite plastic Co., Ltd. アモイ LFT 複合プラスチック有限公司は、LFT&LFRT に焦点を当てたブランド企業です。長ガラス繊維シリーズ (LGF) および長炭素繊維シリーズ (LCF)。同社の熱可塑性LFTはLFT-D成形にも使用できます。お客様のご要望に合わせて製作可能です:長さ5~25mm。同社の長繊維連続浸透強化熱可塑性プラスチックは ISO9001&16949 システム認証に合格しており、製品は多くの国内商標と特許を取得しています。

What is HDPE? High density polyethylene (HDPE) is a white powder or granular product. Non-toxic, tasteless, crystallinity is 80% ~ 90%, softening point is 125 ~ 135℃, the use of temperature can reach 100℃; The hardness, tensile strength and creep property are better than low density polyethylene. Good wear resistance, electrical insulation, toughness and cold resistance; Good chemical stability, at room temperature, insoluble in any organic solvent, acid, alkali and all kinds of salt corrosion resistance; Thin film to water vapor and air permeability is small, low water absorption; Poor aging resistance, environmental stress cracking resistance is not as good as low density polyethylene, especially thermal oxidation will reduce its performance, so the resin must be added in antioxidants and ultraviolet absorbent to improve this deficiency. Filling Long glass fiber The tensile strength of polyethylene can be improved obviously when the amount of glass fiber is 30% ~ 40%. With the continuous increase of the addition amount, the increase of tensile strength did not change significantly, but tended to be stable. The addition amount of glass fiber has a great influence on the elastic modulus of polyethylene plastic materials. With the increase of glass fiber addition amount, the elastic modulus of polyethylene plastic materials will continue to increase and reach a certain value. ガラス繊維の添加は、ポリエチレンプラスチック材料の破断伸びに大きな影響を与えます。ガラス繊維の添加量が増えると、ポリエチレンプラスチック材料の破断点伸びは減少し続けます。一定の値までは、ガラス繊維変性ポリエチレンの脆性がより顕著になり、ガラス繊維の脆性とほぼ同等になります。 ご参考までにTDS 応用 工場 倉庫とパッケージ チームと顧客 私たちはあなたに以下を提供します: 1. LFT & LFRT 材料技術パラメータと最先端の設計。 2. 金型前面の設計と推奨事項。 3. 射出成形、押出成形などの技術サポートを提供します。

PPS The molecular structure of PPS consists of benzene ring and sulfur atoms interarranged, the configuration is orderly, easy to form a high thermal stability of the crystal structure. At the same time, the molecular structure of PPS material has a highly stable chemical bond characteristics, the benzene ring structure makes PPS more rigid, and the sulfur ether bond (-S-) provides a certain degree of flexibility. PPS itself has good heat resistance, flame retardant, chemical resistance, should be a promising material, but unmodified PPS has some unavoidable defects: Difficult processing:  This is the biggest pain point of all high temperature resistant materials -- high processing temperature, no matter the molding process or processing energy consumption, will face great challenges. In addition, PPS is still prone to thermal oxidation crosslinking in the melting process, resulting in reduced fluidity and further improve the processing difficulty; Poor toughness: PPS molecular chain is rigid, the maximum crystallinity is as high as 70%, the elongation is low and the welding strength is not so good. As a result, the impact resistance of unmodified PPS is poor, which limits the application scope. High cost: PPS raw materials and general engineering plastics compared, the price is about 1-2 times higher, and some modified materials compared with low cost performance; Difficult coating: PPS surface coating and coloring performance is not ideal. While this is not a major problem for now, it is a limiting factor. PPS-LGF Long glass fiber reinforced composites can solve your problems when other methods of reinforced plastics do not provide the performance you need or if you want to replace metal with plastic. Long glass fiber reinforced composites can cost-effectively reduce the cost of goods and effectively improve the mechanical properties of engineering polymers, and increase the durability by forming long fibers to form a long-fiber-reinforced internal skeleton network. Performance is preserved in a wide range of environments. 参考のためのTDS 応用 私たちに関しては アモイ LFT 複合プラスチック有限公司は、LFT&LFRT に焦点を当てたブランド企業です。長ガラス繊維シリーズ (LGF) および長炭素繊維シリーズ (LCF)。熱可塑性 LFT は、LFT-G 射出成形および押出成形に使用できるほか、LFT-D 成形にも使用できます。お客様のご要望に合わせて製作可能です:長さ5~25mm。同社の長繊維連続浸透強化熱可塑性プラスチックは ISO9001&16949 システム認証に合格しており、製品は多くの国内商標と特許を取得しています。

PLA素材とは何ですか? ポリ乳酸 (PLA) は、トウモロコシやキャッサバなどの再生可能な植物資源から抽出されたデンプンから作られる、新しいバイオベースの再生可能な生分解性素材です。 でんぷん原料を糖化してグルコースを得、そのグルコースと特定の菌株を発酵させて高純度の乳酸を生成し、化学合成により一定の分子量のポリ乳酸を得る重合連鎖は次のとおりです。 デンプン（精製） -- - > グルコース（発酵） -- - > 乳酸（環状） -- - > ラクチド（重合） -- - > PLA PLAは、21世紀において最も大きな発展の可能性を秘めた「グリーンプラスチック」です。優れた機械的特性と透明性を備えていますが、結晶化速度が遅い、耐熱性が低いなどの欠点があり、普及と使用が制限されています。したがって、性能を向上させるために何らかの強化方法がよく使用されますが、透明性や複雑なプロセスが犠牲になります。 PLA LGF素材とは何ですか? The rigidity of the fiber makes it play the role of skeleton support in the polymer matrix. When the polymer is heated, the movement of the chain segment is limited, thus improving the heat resistance of the material At present, carbon fiber and glass fiber can be used to enhance the modification of PLA. Among these fibers, carbon fiber and glass fiber are widely used because of their high strength and modulus. The composite material was prepared by adding fiber into PLA. After heat treatment, the modification effect of the composite material was the best, and the heat resistance temperature was increased by nearly 40℃ compared with that of pure PLA. Two or more materials with synergistic effect can be added at the same time to improve the thermal performance of PLA. The test results show that the Vica softening temperature of the composites exceeds 140℃. Production process Details Other products you may wonder                        PP-LGF                                  PA6-LGF                                   TPU-LGF             Frequently asked questions Q. Does long glass fiber and long carbon fiber injection have special requirements for injection molding machines and molds? A. There are certainly requirements. Especially from the product design structure, as well as the injection molding machine screw nozzle and mold structure injection molding process must consider the requirements of long fiber. Q. The product is easy to brittle, so changing to use long fiber reinforced thermoplastic materials can solve this problem? A. The overall mechanical properties must be improved. The characteristics of long glass fiber and long carbon fiber are the advantages in mechanical properties. It has 1-3 times higher (toughness) than short fiber, and the tensile strength (strength and rigidity) is increased by 0.5-1 times. Q. When a customer want to develop a new product, how to recommend customers suitable material and characteristics? A. 新製品については、お客様の技術要件、使用環境、試験条件などを把握し、各種長繊維樹脂基材の特性に応じた機種を推奨する必要があります。

PA12 PA12 polyamide or nylon 12 Chemical and physical properties of PA12 PA12 is a linear, semi-crystalline - crystalline thermoplastic material from butadiene. Its properties are similar to PA11, but its crystal structure is different. PA12 is a good electrical insulator and will not be affected by moisture as other polyamides. PA12 has good impact resistance mechanical and chemical stability. There are many improved varieties of PA12 in terms of plasticizing and reinforcing properties. Compared with PA6 and PA66, these materials have lower melting point and density, and have very high moisture recovery. PA12 has no resistance to strong oxidizing acids. The viscosity of PA12 depends mainly on humidity, temperature and storage time. PA12 It's very liquid. The shrinkage rate of PA12 is between 0.5% and 2%, depending on the variety of PA12 material, wall thickness and other process conditions. PA12 compounds plastic Nylon glass fiber material is a kind of composite material, adding glass fiber on the basis of the original nylon material, so that the material has the following characteristics: High temperature resistance, good dimensional stability, good toughness, good insulation, corrosion resistance, high mechanical strength. LGF & SGF Compared with the short fiber, it has more excellent performance in mechanical properties. It is more suitable for large products and structural parts. It has 1-3 times higher (toughness) than short fiber, and the tensile strength (strength and rigidity) is increased by 0.5-1 times. Datasheet for reference Application ■ Power tools: cutting machine, electric saw, electric drill, Angle grinder, polishing machine, electric hammer, electric pick, hot air gun and other models; ■ Automotive industry: cooling chamber, intake manifold, frame bracket, ventilation grille, door handle, throttle body and other models; ■ 機械産業: ウォーターポンプ、ウォーターバルブ、ベアリング、シャフトスリーブ、ギア、ブラケットなどのモデル。 ■ スポーツ用品：スキー用品、ベビーカー、フィットネス用品部品、その他のモデル。 ■ 事務機器：シートブラケット、プーリー、回転軸、シュレッダーギア、プリンター部品、その他のモデル。 認証 工場 パッケージ 私たちを選ぶ理由

PPA material High temperature nylon is a semi-aromatic polyamide polymer made from terephthalic acid or phthalic acid and aliphatic diamine through polycondensation reaction. Its molecular chain contains benzene ring and diamine flexible long chain, so it has a high crystallization rate and crystallinity. PPA engineering plastics are high performance engineering plastics reinforced by fiber with high temperature nylon as the base material. The structure and crystallization properties of high temperature nylon make it have more characteristics and excellent overall performance than nylon 66 and nylon 6 and other engineering plastics: strong rigidity, high hardness, high temperature resistance, good chemical resistance and low water absorption, dimensional accuracy and stability and low warpiness, excellent fatigue resistance, in many fields including automotive parts, Mechanical parts and electrical and electronic parts are widely used in motor parts, circuit breakers and so on. PPA-LGF material 1、強くて硬い、強い剛性、高硬度、低い反り 2、良い靭性 3、良い耐薬品性 良い耐薬品性 4、PPAは吸水率の影響を受け、優れた寸法精度、安定性、低い反りを持っています 5、小さな浮き、表面はスプレーおよび電気めっきが可能です。 6、金属との結合力が高く、鉄プラスチックの分離時の温度変化とサイズの成形を防ぎます。 TDS は参考のみ 生産工程 応用 低圧スイッチ、サーキットブレーカー、機械部品、自転車アクセサリーなど 私たちに関しては アモイ LFT 複合プラスチック有限公司は、LFT&LFRT に焦点を当てたブランド企業です。長ガラス繊維シリーズ (LGF) および長炭素繊維シリーズ (LCF)。同社の熱可塑性 LFT は、LFT-G 射出成形および押出成形に使用できるほか、LFT-D 成形にも使用できます。お客様のご要望に応じて長さ5～25mmまで製作可能です。同社の連続浸透強化熱可塑性プラスチックは ISO9001&16949 システム認証に合格しており、製品は多くの国内商標と特許を取得しています。

MXD6 Polyadipyl-m-benzoylamine, referred to as mxd6, generally referred to as "nylon mxd6", resin than other engineering plastics have higher mechanical strength and modulus, is also a special high barrier nylon material. Although the barrier of mxd6 is slightly worse than that of pvdc and evoh, its barrier is not affected by temperature and humidity, which is especially suitable for high temperature and humid occasions. In today's barrier packaging and plastic instead of steel general trend, nylon mxd6 has become one of the most eye-catching new plastic varieties. Structure performance: PA MXD6 nylon material has high strength, high rigidity, high thermal deformation temperature, small thermal expansion coefficient; Dimensional stability, low water absorption rate and small size change after water absorption, mechanical strength changes less; Forming shrinkage is small, suitable for precision forming processing; Excellent coating performance, especially suitable for high temperature surface coating; Excellent barrier to oxygen, carbon dioxide and other gases. Excellent mechanical and thermal properties and high strength, high modulus and heat resistance, high barrier, excellent cooking resistance Advantages 1、Maintain high strength and rigidity in a wide temperature range 2、High heat deflection temperature, small coefficient of thermal expansion 3、Low water absorption, small size change after water absorption, less mechanical strength reduction 4、Small shrinkage rate of molding, suitable for precision molding process 5、Excellent paintability, especially suitable for surface painting under high temperature 6、Excellent barrier to oxygen, carbon dioxide and other gases MXD6-LGF MXD6 applications in the plastics modification industry MXD6 can be compounded with glass fibers, carbon fibers, minerals and/or advanced fillers for materials containing 50-60% glass fiber reinforcement with exceptional strength and stiffness. Even when filled with high levels of glass fiber, its smooth, resin-rich surface creates a high gloss finish like no glass fiber, making it ideal for painting, metal coating or creating naturally reflective housings. 1、High fluidity for thin wall It is a very high flowing resin that can easily fill thin walls as thin as 0.5 mm thick even with glass fiber content as high as 60%. 2、Excellent surface finish The resin-rich perfect surface has a highly polished appearance, even with a high glass fiber content. 3、Very high strength and stiffness MXD6 with 50-60% glass fiber reinforcement has a tensile and flexural strength similar to many cast metals and alloys. 4、Good dimensional stability At ambient temperature, the coefficient of linear expansion (CLTE) of MXD6 glass fiber composite is similar to that of many cast metals and alloys. It is highly reproducible due to low shrinkage and the ability to maintain tight tolerances (length tolerances can be as low as ± 0.05% if properly formed). TDS for reference only Application MXD6 replaces metal to make high quality structural parts for automobiles, electronics and electrical appliances 自動車部品では機械的強度が高く、耐油性に優れ、120～160℃の範囲で長時間使用できる材料製品が求められる場面が多くあります。ガラス繊維強化MXD6は、225℃までの耐熱性と高温下での強度保持率が高く、自動車エンジンのシリンダーブロック、シリンダーヘッド、ピストン、シンクロギヤ等に使用されています。MXD6/PPOアロイは、高温耐性、高強度、耐油性、耐摩耗性、寸法安定性などの特性を備えており、自動車ボディの垂直外板、前後フェンダー、ホイールカバーなどに使用でき、プレス成形ではほとんど不可能です。鋼板。自動車の湾曲部分やシャーシ。 私たちに関しては

Polyphenylene sulfide PPS is one of the typical representatives of special engineering plastics, with a linear structure of alternating benzene rings and sulfur atoms. In the condensed structure, PPS is easy to crystallize, crystallinity of nearly 70%, therefore, has good thermal stability, chemical stability and dimensional stability, etc. PPS mainly has the following five performance advantages. (1) excellent heat resistance. pps melting point of more than 280 ℃, heat deflection temperature of more than 260 ℃, and after high-temperature heat aging treatment, the strength retention rate is high. (2) since the flame retardant. PPS itself has flame retardant, without adding flame retardants flame retardant level can reach UL94 V- 0 level. (3) good mechanical properties. PPS is a brittle material, has good creep resistance, high surface hardness, good wear resistance, and carbon fiber and other materials compound, but also shows good self-lubricating properties. (4) excellent chemical resistance, irradiation resistance. pps below 200 ℃ almost insoluble in any solvent, can withstand almost all inorganic substances, radiation dose up to 108Gy. (5) good processing properties. pps melt viscosity is low, as the resin matrix of composite materials, for the reinforcement of the flow of excellent wetting effect. As PPS has the above performance advantages, and compared to other high-performance thermoplastic resins and easy processing, low cost, so become an excellent resin matrix for the manufacture of composite materials. Long glass fiber Glass fiber is an inorganic non-metallic material with excellent performance, is a natural mineral with silica as the main raw material, add specific metal oxide mineral raw materials, mixed evenly, molten at high temperature, molten glass liquid flow through the funnel outflow, in the role of high-speed pull gravitational force is drawn and rapidly cooled and cured into a very fine continuous fiber. Glass fiber monofilament diameter from a few microns to more than twenty microns, equivalent to a hair of 1/20-1/5, each bundle of fiber original filament are composed of hundreds or even thousands of monofilaments. Glass fiber basic properties: The appearance of a smooth cylindrical surface, the cross-section is a complete circle, round cross-section to withstand the load capacity; gas and liquid through the resistance is small, but the surface is smooth so that the holding force of the fiber is small, not conducive to the combination with the resin; density is generally in 2.50-2.70 g/cm3, depending mainly on the glass composition; tensile strength than other natural fibers, synthetic fibers to be high; brittle materials, the elongation at break is very small ; water resistance and acid resistance is good, while alkali resistance is poor. It can be divided into continuous glass fiber, short glass fiber (SGF) and long glass fiber (LGF) by length classification. Long glass fiber is the most widely used glass fiber at present. And Xiamen LFT plastic composite company is focuses on the produce of long glass fiber compounds for many years. SGF VS LGF 1. サイズの長さの違い エンジニアリング材料の長いガラス繊維と短いガラス繊維は、文字通りサイズの長さの違いを意味します。より一般的な短いガラス繊維のサイズは約 0.2mm ～ 0.6mm です。長いガラス繊維のサイズは約6mm〜25mmです。 2. 性能強度の違い ガラス繊維の長さが異なると性能強度が異なり、複合材料内の長いガラス繊維の繊維長は、短いガラス繊維よりも衝撃強度が高くなります。 3. 製造プロセスが異なります 長ガラス繊維の製造では、原料に対する高い要求があり、特に製造プロセスではガラス繊維の表面を活性化する必要があり、加工中にガラス繊維を浸み込ませることができず、外部漏れ現象が発生します。ガラス短繊維の製造は、一般にサイズに特別な要件がないため、製造が比較的容易であり、原材料の要件がそれほど高くなく、製造業者の製造コストが低い。 4. さまざまな製造および加工方法 長ガラス繊維の製造および加工方法には、一般に射出成形と成形が使用されます。一方、最も短いガラス繊維の射出成形法。 製品プロセス TDS は参考のみ 詳細 番号 色 長さ サンプル パッキング MOQ 積荷港 納期 PPS-NA-LGF40 元の色 (または必要に応じて) 12mm (または必要に応じて) 利用可能 25kg/袋 25kg 厦門港 発送後7~15日 私たちを選ぶ理由 1. LFTおよびLFRT材料の技術パラメータと最先端の設計 2. 金型正面の設計と推奨事項 3.射出成形、押出成形などの技術サポートを提供します。

PLAプラスチック ポリ乳酸（PLA）は優れた生分解性素材の一種で、主に再生可能な植物資源（トウモロコシ、ジャガイモなど）のデンプンから製造され、包装、農業、食器、医療、日用不織布などの分野で広く使用されています。加工特性、物理的特性、機械的特性、生体適合性、生分解性が優れているため、材料に優れています。主なマトリックスとして PLA を使用した多機能複合材料の調製に関する研究は、分解性材料の開発における現在のホットスポットです。 長ガラス繊維 PLAは通常のポリマーと同様に押出成形、注型成形、フィルムブロー成形、射出成形、ボトルブロー成形、ファイバー成形などの加工が可能です。作製されたフィルム、シート、繊維は、二次加工を経て、衣類、繊維、不織布、包装、農業、林業、土木建築、医療・衛生用品、日用品など幅広い用途に使用できます。過熱や回転など。PLA製品は使用後、有機資源、物理的リサイクル、埋め立て、サーマルリサイクル、またはケミカルリサイクルによってリサイクルすることができます。 他の方法の強化プラスチックでは必要な性能が得られない場合、または金属をプラスチックに置き換えたい場合は、長ガラス繊維強化複合材料が問題を解決します。ガラス長繊維強化複合材料は、製品コストを効果的に削減し、エンジニアリングポリマーの機械的特性を効果的に改善し、長繊維を形成して長繊維強化内部骨格ネットワークを形成することにより耐久性を向上させることができます。幅広い環境下でパフォーマンスを維持します。 バイオベースのポリ乳酸 (PLA) 熱可塑性プラスチックは比較的環境に優しく、リサイクルが簡単ですが、グラスファイバーなどの複合材料ははるかに強力です。現在では、新しい PLA 複合材料を使用して両方の利点を組み合わせることができます。 PLA-LGFディスプレイ 製品プロセス 認証 品質マネジメントシステム ISO9001/1949認証取得 国立研究所認定証明書 変性プラスチック革新企業 名誉証明書 重金属 REACH および ROHS テスト 私たちに関しては アモイ LFT 複合プラスチック有限公司は、LFT&LFRT に焦点を当てたブランド企業です。長ガラス繊維シリーズ (LGF) および長炭素繊維シリーズ (LCF)。同社の熱可塑性 LFT は、LFT-G 射出成形および押出成形に使用できるほか、LFT-D 成形にも使用できます。お客様のご要望に応じて長さ5～25mmまで製作可能です。同社の連続浸透強化熱可塑性プラスチックは ISO9001&16949 システム認証に合格しており、製品は多くの国内商標と特許を取得しています。 よくあるご質問 Q. 長繊維強化熱可塑性材料を使用する場合、補強方法や材料の長さはどのように選べばよいですか？ A. 材料の選択は製品の要件によって異なります。製品の性能要件に応じて、コンテンツをどの程度強化するか、どの程度の長さが適切であるかを把握する必要があります。 Q. どのような状況で長繊維が短繊維に取って代わることができますか? 一般的な代替材料は何ですか? A. お客様の機械的特性が満たせない場合、またはより高級な金属の代替品が必要な場合は、従来の短繊維材料を長ガラス繊維および長炭素繊維の LFT 材料に置き換えることができます。たとえば、ナイロン強化ガラス繊維の代わりに PP ガラス長繊維が使用されることが多く、PPS シリーズの代わりにナイロン長ガラス繊維が使用されています。 Q. 射出成形製品用の長炭素繊維には特別なプロセス要件はありますか? A. 射出成形機のスクリューノズル、金型構造、射出成形プロセスに使用する長炭素繊維の要件を考慮する必要があります。長炭素繊維は比較的高コストの材料であるため、選択プロセスでは性能の問題とコストを評価する必要があります。

PA12 の紹介 PA12 の学名はポリドデカラクタムで、ナイロン 12 としても知られています。その重合の基本原料はブタジエンであり、石油化学製品に依存する場合があります。これは半結晶質から結晶質の熱可塑性材料です。その特性は PA11 と似ていますが、結晶構造が異なります。PA12 は優れた電気絶縁体であり、他のポリアミドと同様に、湿気による絶縁特性の影響を受けません。PA12 は、多くの改善された可塑化特性と強化特性を備えています。 PA6 や PA66 と比較して、これらの材料は融点と密度が低く、水分回収率が非常に高いです。PA12 は強酸化性の酸に対して耐性がありません。とてもよく流れます。収縮率は 0.5% ～ 2% ですが、主に材料の種類、壁の厚さ、その他のプロセス条件によって異なります。 PA12-長ガラス繊維 ナイロンガラス繊維材料は、元のナイロン材料をベースにガラス繊維を加えた複合材料であり、材料に次の特性を持たせます：高温耐性、良好な寸法安定性、良好な靭性、良好な絶縁性、良好な耐食性、および 高い機械的強度。 参考のためのTDS ナイロン 12 は最も広く使用されている長炭素鎖ナイロンで、低吸水性に加えてナイロンの一般的な特性をほとんど備えており、高い寸法安定性、高温耐性、耐食性、優れた靭性、加工が容易という利点があります。 。同じく長鎖炭素鎖のナイロン材料であるPA11と比較して、PA12の原料ブタジエンはPA11の原料ヒマシ油の価格のわずか3分の1であり、PA11の代わりにほとんどのシナリオで使用でき、自動車などの多くの分野で広く使用されています。燃料ライン、エア ブレーキ ホース、海底ケーブル、3D プリントなど。 出願済み 自動車、スポーツ部品、太陽エネルギー、太陽光発電産業、その他の産業に適しています。 PA12シリーズ パッケージ 私たちに関しては アモイ LFT 複合プラスチック有限公司は、LFT&LFRT に焦点を当てたブランド企業です。長ガラス繊維シリーズ (LGF) および長炭素繊維シリーズ (LCF)。同社の熱可塑性 LFT は、LFT-G 射出成形および押出成形に使用できるほか、LFT-D 成形にも使用できます。お客様のご要望に応じて長さ5～25mmまで製作可能です。同社の連続浸透強化熱可塑性プラスチックは ISO9001&16949 システム認証に合格しており、製品は多くの国内商標と特許を取得しています。

PP fill Long glass fiber Advantages of glass fiber reinforced PP material in modified PP material. 1、The heat resistance temperature of glass fiber reinforced PP is much higher. 2、The shrinkage of glass fiber reinforced PP decreases a lot, and the rigidity is greatly improved. 3, glass fiber reinforced PP plastic, will not stress cracking, impact resistance improved a lot. 4、After glass fiber reinforced, the burning performance of PP plastic is reduced a lot. 5、After glass fiber reinforcement, the strength of PP is improved, such as: tensile strength, compressive strength, bending strength. The disadvantages of glass fiber reinforced PP material in modified PP material. 1、After glass fiber reinforcement, the transparency of the material decreases. 2、After glass fiber reinforced, the toughness of PP decreases and the brittleness increases. 3、After glass fiber reinforced, the hygroscopic property of PP is greatly enhanced, therefore, it should be dried when injection molding. 4、After glass fiber reinforcement, the melt viscosity of PP increases, the fluidity becomes worse, and the injection pressure increases a lot. 5、After glass fiber reinforcement, the fluidity of PP material is poor, and the injection temperature of reinforced plastic is increased by 10℃-30℃. 6、After glass fiber reinforced, attention should be paid to the surface corrosion treatment and surface hardness treatment of the equipment. 7、ガラス繊維強化後、射出工程中にガラス繊維がプラスチック製品の表面に入り込み、製品の表面が粗くなることがあります。プラスチックポリマーが製品の表面に入り込み、より高い表面品質を得ることができるように、射出成形時に金型を加熱するために金型温度機械を使用する必要があります。 TDS は参考のみ 一般グレード、耐熱グレード、耐紫外線グレード、耐強化グレードを取り揃えております。 応用 一般グレード：自動車部品、洗濯機部品、ウォーターポンプ部品、水処理部品、家具部品など。 耐熱グレード：自動車の前後モジュール、水タンクフレーム、バッテリーブラケット、エンジンカバー、天窓フレームなど 耐紫外線グレード：車のハンドル、車のミラー部品、バッテリーケース、トラックの社外ペダルなど。 耐強化グレード：電動工具、ポンプシェル、管継手など LGF VS SGF よくある質問 Q. 長ガラス繊維と長炭素繊維の射出成形には、射出成形機や金型に特別な要件がありますか? A. 確かに要件はあります。特に製品設計構造、射出成形機のスクリューノズル、金型構造から、射出成形プロセスでは長繊維の要件を考慮する必要があります。 Q. ガラス長繊維、炭素長繊維製品の繊維浮きの原因と解決策について教えてください。 A. ゾルの温度または金型の温度が低く、射出成形圧力が低いため、ガラス繊維と樹脂は十分に相溶して拡散できません。金型表面の温度が不均一であると繊維浮きの問題が発生しますが、ゾル温度、金型温度、射出圧力を高くすることで解決できます。 Q. 長ガラス繊維強化PPを使用すると、材料の靭性が低下し、脆くなります。この問題を解決する方法はありますか? A. 長ガラス繊維と長炭素繊維により、基材の衝撃強度と引張強度が大幅に向上します。

PPA-LGF PPA (正式名ポリフタルアミド) は、原料としてテレフタル酸またはフタル酸を 55% 以上含む半芳香族ポリアミドで、一般に芳香族高温ナイロンとして知られています。PPA は、従来の脂肪族ナイロン (PA6/PA66) 材料と比較して、優れた機械的特性と高温耐性を備えています。PPA 材料は、吸水性が比較的低く、寸法安定性と耐食性に優れています。 ガラス繊維強化 PPA 複合材料は、高温耐性、高強度、低密度を備えており、スチールをプラスチックに置き換える最適な樹脂と考えられています。従来の短繊維強化ペレットと比較して、長ガラス繊維強化 PPA 複合材料は優れた物理的および機械的特性を備えています。 応用 高温ナイロンは過酷な環境における高強度、高荷重、高温に耐えることができるため、エンジン領域 (エンジン カバー、スイッチ、コネクタなど) やトランスミッション システム (ベアリング ケージなど) での用途に最適です。 、空気システム (排気制御システムなど)、および吸気ユニット。 PPAエンジニアリングプラスチックは、耐熱ナイロンを基材として繊維強化した高性能エンジニアリングプラスチックです。高温ナイロンの構造と結晶特性により、ナイロン 66 やナイロン 6、その他のエンジニアリング プラスチックよりも多くの特性と優れた総合性能を備えています。つまり、強い剛性、高硬度、高温耐性、良好な耐薬品性、低吸水性、寸法精度などです。安定性と反りの少なさ、耐疲労性に優れ、自動車部品、機械部品、モーター部品に使用される電気・電子部品など多くの分野で幅広く使用されています。サーキットブレーカーなど LGF VS SGF 気になるその他の素材 私たちに関しては アモイ LFT 複合プラスチック有限公司は、LFT&LFRT に焦点を当てたブランド企業です。長ガラス繊維シリーズ (LGF) および長炭素繊維シリーズ (LCF)。同社の熱可塑性 LFT は、LFT-G 射出成形および押出成形に使用できるほか、LFT-D 成形にも使用できます。お客様のご要望に応じて長さ5～25mmまで製作可能です。同社の連続浸透強化熱可塑性プラスチックは ISO9001&16949 システム認証に合格しており、製品は多くの国内商標と特許を取得しています。 ご提供させていただきます 1. LFT&LFRT材料の技術パラメータと最先端の設計 2. 金型正面の設計と推奨事項 3. 射出成形、押出成形等の技術サポートの提供