MXD6 introduction Polyhexanediyl m-dimethylamine, referred to in English as mxd6, generally referred to as "nylon mxd6", the resin has higher mechanical strength and modulus than other engineering plastics, but also a special high barrier nylon material. Nylon mxd6 is one of aromatic and aliphatic polyacyl limbs, which is produced by m-phenylenedimethylamine and adipic acid. In industrial production, in order to make the raw materials economical and easy to obtain, often mixed xylene as raw materials, first made of m-phenylene dimethylamine content higher than 70% of mixed benzene dimethylamine, and then with adipic acid to generate salt, in the presence of a small amount of stabilizer adipic acid and appropriate amount of water for the pressure condensation reaction, the resulting polymer is a hybrid. Although the barrier property of mxd6 is a little less than that of pvdc and evoh, its barrier property is not affected by temperature and humidity, which is especially suitable for high temperature and humid occasions. In today's barrier packaging and the general trend to replace steel with plastic, nylon mxd6 has become one of the striking new plastic varieties. Advantages 1、Maintain high strength and rigidity in a wide temperature range 2、High heat deflection temperature, small coefficient of thermal expansion 3、Low water absorption, small size change after water absorption, less mechanical strength reduction 4、Small shrinkage rate of molding, suitable for precision molding process 5、Excellent paintability, especially suitable for surface painting under high temperature 6、Excellent barrier to oxygen, carbon dioxide and other gases Long glass fiber compounds Long glass fiber reinforced composites can solve your problems when other methods of reinforced plastics do not provide the performance you need or if you want to replace metal with plastic. Long glass fiber reinforced composites can cost-effectively reduce the cost of goods and effectively improve the mechanical properties of engineering polymers, and increase the durability by forming long fibers to form a long-fiber-reinforced internal skeleton network. Application MXD6 can be filled with glass fibers to create a glass fiber reinforced material containing 20-60% glass fiber with exceptional strength and stiffness. Even when filled with high levels of glass fiber, its smooth, resin-rich surface creates a high gloss surface as without glass fiber, making it ideal for painting, metal coating or creating naturally reflective housings. 1、High fluidity for thin wall It is a very high flowing resin that can easily fill thin walls as thin as 0.5 mm in thickness even when the glass fiber content is as high as 60%. 2、Excellent surface finish The resin-rich perfect surface has a highly polished appearance, even with a high glass fiber content. 3、Very high strength and stiffness With 50-60% glass fiber reinforcement, MXD6 has tensile and flexural strengths similar to many cast metals and alloys. 4、Good dimensional stability At ambient temperature, the coefficient of linear expansion (CLTE) of MXD6 glass fiber composite is similar to that of many cast metals and alloys. It is highly reproducible due to low shrinkage and the ability to maintain tight tolerances (length tolerances can be as low as ± 0.05% if properly formed). MXD6 replaces metal in the production of high-quality structural parts for automobiles, electronics, and appliances In automotive parts, many occasions require material products with high mechanical strength and good oil resistance, and can be used in the range of 120 ~ 160 ℃ for a long time. Glass fiber reinforced MXD6 has a heat resistance of up to 225°C and high strength retention at high temperatures, and can be used in cylinder blocks, cylinder heads, pistons, timing gears, etc. of automobile engines. MXD6/PPO alloy has the properties of high temperature resistance, high strength, oil resistance, wear resistance, good dimensional stability, etc. It can be used for vertical outer panels of automobile bodies, front and rear fenders, wheel covers and curved parts that can hardly be formed by stamping with steel plates and automobile chassis. TDS foryour reference Certifications Quality Management System ISO9001/1949 Certification 国立研究所認定証明書 変性プラスチック革新企業 名誉証明書 重金属 REACH および ROHS テスト アモイLFT複合プラスチック有限公司 アモイ LFT 複合プラスチック有限公司は、LFT&LFRT に焦点を当てたブランド企業です。長ガラス繊維シリーズ (LGF) および長炭素繊維シリーズ (LCF)。同社の熱可塑性 LFT は、LFT-G 射出成形および押出成形に使用できるほか、LFT-D 成形にも使用できます。お客様のご要望に応じて長さ5～25mmまで製作可能です。同社の連続浸透強化熱可塑性プラスチックは ISO9001&16949 システム認証に合格してお�

PBTの紹介 学名：ポリブチレンテレフタレート、PBTはポリエステル系に属し、1.4pbtブチレングリコールとテレフタル酸（PTA）またはテレフタル酸エステル（DMT）を重縮合させ、混合工程を経て乳白色半透明から不透明に作られます。結晶性熱可塑性ポリエステル樹脂。PET と合わせて、熱可塑性ポリエステル、または飽和ポリエステルと呼ばれます。 プロセス PBTの結晶化速度が速く、最も適した加工方法は射出成形ですが、その他の方法としては押出成形、ブロー成形、コーティング、各種二次加工成形などが挙げられます。 長ガラス繊維コンパウンド 他の方法の強化プラスチックでは必要な性能が得られない場合、または金属をプラスチックに置き換えたい場合は、長ガラス繊維強化複合材料が問題を解決します。ガラス長繊維強化複合材料は、コスト効率よく製品コストを削減し、エンジニアリングポリマーの機械的特性を効果的に改善し、長繊維を形成して長繊維強化内部骨格ネットワークを形成することで耐久性を向上させることができます。 ご参考までにTDS 応用 その他のアプリケーションについては、当社までご連絡ください。専門的な技術アドバイスを提供いたします。 気になるその他の素材                          PA12-LGF HDPE-LGF  TPU-LGF                                                                                                                                              詳細 番号 色 長さ サンプル MOQ パッケージ 積荷港 納期 PBT-NA-LGF30 オリジナルカラー（カスタマイズ可能） 約12mm (カスタマイズ可能) 利用可能 25KG 25kg/袋 厦門港 発送後7-15日 よくある質問_ Q. 長繊維強化熱可塑性材料を使用する場合、補強方法と材料の長さはどのように選択すればよいですか? A. 材料の選択は製品の要件によって異なります。製品の性能要件に応じて、内容をどの程度強化するか、どの程度の長さが適切であるかを判断する必要があります。 Q. 射出成形に適しているだけでなく、長繊維製品は押出成形などの加工も可能ですか? A. LFT長ガラス繊維と長炭素繊維は主に射出成形に使用されますが、さまざまな熱可塑性プラスチック成形方法でプレートプロファイルチューブやモールドエッジを押出成形することもできます。 Q. 長繊維製品はコストが高くなります。リサイクル価値は高いですか？ A. 熱可塑性 LFT 長繊維素材はリサイクルして再利用することができます。

PA66-LGF Information PA66 is one of the most produced and widely used polyester series products. It has high grain size, excellent tensile properties, bending properties, tensile strength and other material mechanical properties, and its excellent ultra-low temperature characteristics and organic chemical properties. It is a class of rubber products with wide range of application, stable characteristics, good mechanical properties, high quality insulation, low density, easy processing and molding, self-extinguishing, and good wear resistance. Therefore, it is widely used in vehicles, electronic and electrical, chemical materials, industrial equipment, instrument panels, construction projects and other industries. However, it has high water absorption, poor alkali resistance, dry ultra-low temperature impact, low compressive strength and easy to deform after absorbing moisture, which affects the reliability of goods specifications. People have improved PA66 in a variety of ways, adding PA66 chemical fiber is one of them. After adding glass fiber, its impact force, heat deformation, material mechanical properties, molding processability and acid resistance are significantly improved. Glass fiber is a class of functional raw materials with high quality characteristics. This utility model has the advantages of low cost, non-combustibility, high temperature resistance, acid resistance, high tensile strength, high impact compressive strength, low tensile strength, high quality insulation properties, high quality insulation properties, etc. It is usually used as a raw material to improve organic chemical polymers or functional materials and composites. 原材料に対する比例制限による最も重要な危険は、機械的特性です。改質 PA66 の材料の機械的特性は、ガラス繊維の組成にも関連しています。PA66 の引張強度、曲げ強度、衝撃圧縮強度は、PA66 化学繊維の添加後のガラス繊維組成に応じて増加します。管理されたシステムの引張強度と曲げ強度は直線的に増加しましたが、ガラス繊維の組成は 30% でした。引張強度と曲げ強度が増加する傾向は、ある程度の改善を示しました。結果は、PA66 が合理的なページ層を生成し、マトリックスとページ間の接地応力を合理的に伝達できるため、マトリックスの圧縮強度を向上できることを示しています。 PA66-LGF TDS データシートは厦門 LFT によってテストされたもので、参照のみを目的としています。 PA66-LGF アプリケーション 多くの分野、その他の用途に適しています。技術的なアドバイスをお問い合わせください。 詳細 番号 色 長さ サンプル MOQ 積荷港 納期 支払い条件 PA66-NA-LGF30 オリジナルカラー（カスタマイズ可能） 12mm (カスタマイズ可能) 利用可能 25kg 厦門港 発送後7-15日 議論しました 厦門L FT複合プラスチック有限公司 アモイL FT複合プラスチック有限公司は、LFT&LFRT に焦点を当てたブランド企業です。長ガラス繊維シリーズ (LGF) および長炭素繊維シリーズ (LCF)。同社の熱可塑性 LFT は、LFT-G 射出成形および押出成形に使用できるほか、LFT-D 成形にも使用できます。お客様のご要望に応じて長さ5～25mmまで製作可能です。同社の長繊維連続浸透強化熱可塑性プラスチックは ISO9001 &16949 システム認証に合格しており、製品は多くの国内商標と特許を取得しています。 私たちはあなたに提供します: 1. LFT&LFRT材料の技術パラメータと最先端の設計 2. 金型正面の設計と推奨事項 3. 射出成形、押出成形などの技術サポートを提供します。

PP素材とは何ですか？  ポリプロピレン (PP) は、PP に添加剤を加えたり、独自の方法で製造したりすることで、独自の用途要件を満たすように変更およびカスタマイズできるため、プラスチック業界の「鋼」材料と呼ばれることがよくあります。 コポリマーPP素材とは何ですか? PP ホモポリマーと比較して、コポリマーポリプロピレンは光学特性が向上し、耐衝撃性が向上し、柔軟性が向上し、溶融温度が低くなり、したがって熱融着温度も低くなります。一方、化学的安定性、水蒸気バリア性、臓器感覚特性の点では基本的にホモポリマーと同じです。 COPO-PP VS HOMO-PP COPO-PP 利点: 良好な総合性能、高強度、高剛性、良好な耐熱性、良好な寸法安定性、優れた低温靱性(良好な柔軟性)、良好な透明性および良好な光沢。 短所： ホモポリマーPPより耐熱性が劣る。 HOMP-PP 利点: 強度が優れています。 欠点: 耐衝撃性が低い (より脆い)、靭性が低い、寸法安定性が低い、老化しやすい、長期熱安定性が低い。 どちらも提供可能ですので、必要な場合はお問い合わせください。 COPO-PPのデータシート COPO-PPの適用 一般グレード：自動車部品、洗濯機部品、ウォーターポンプ部品、水処理部品、家具部品など。 耐熱グレード：自動車の前後モジュール、水タンクフレーム、バッテリーブラケット、エンジンカバー、天窓フレームなど 耐紫外線グレード：車のハンドル、車のミラー部品、バッテリーケース、トラックの社外ペダルなど。 耐強化グレード：電動工具、ポンプシェル、管継手など 他のアプリケーションが提出されている場合は、技術サポートについてお問い合わせください。 アモイLFT複合プラスチック有限公司について アモイ LFT 複合プラスチック有限公司は、LFT&LFRT に焦点を当てたブランド企業です。長ガラス繊維シリーズ (LGF) および長炭素繊維シリーズ (LCF)。同社の熱可塑性 LFT は、LFT-G 射出成形および押出成形に使用できるほか、LFT-D 成形にも使用できます。お客様のご要望に合わせて製作可能です:長さ5~25mm。同社の長繊維連続浸透強化熱可塑性プラスチックは ISO99001&16949 システム認証に合格しており、製品は多くの国内商標と特許を取得しています。 研究室の一部 衝撃強度試験、密度・メルトフローレート試験、熱変形温度試験、ビカット軟化温度試験などを行っております。 今すぐお問い合わせください

ABS ABS resin is a thermoplastic polymeric structural material with high strength, good toughness and easy processing and molding. Long glass fiber reinforced ABS granules Long glass fiber reinforced plastic is based on the original pure plastic, adding long glass fiber and other additives, so as to improve the scope of use of the material. Generally speaking, most of the long glass fiber reinforced materials are mostly used in the structural parts of products, which is a structural engineering material, such as PP, ABS, PA66, PA6, PBT, PPS, etc. Advantages After long glass fiber reinforced,  long glass fiber is a high temperature resistant material, therefore, the heat resistance temperature of reinforced plastics is much higher than before without long glass fiber. After long glass fiber reinforced, the addition of long glass fiber restricts the movement of polymer chains between plastics, so the shrinkage of reinforced plastics is much lower and the rigidity is much higher. After long glass fiber reinforcement, the reinforced plastic will not be stress cracked, and the impact resistance of the plastic will be improved. After long glass fiber reinforcement, long glass fiber is a high-strength material, which also greatly improves the strength of plastic, such as: tensile strength, compression strength, bending strength, much higher. After the long glass fiber reinforcement, the burning performance of the reinforced plastic decreases a lot due to the addition of long glass fiber and other additives, and most of the materials cannot be ignited, which is a kind of flame retardant material. Datasheet for reference Application Can be used at many fields. For more details, please contact us. Other products you may wonder                                                                                                                                                                               PP-NA-LGF                              PA6-NA-LGF                           TPU-NA-LGF                     Frequently asked questions Q. What are the differences and advantages of long fiber materials and thermosets and staple fibers? A. Compared with the short fiber, it has more excellent performance in mechanical properties. It is more suitable for large products and structural parts. It has 1-3 times higher toughness than short fiber, and the tensile strength (strength and rigidity) is increased by 0.5-1 times. Compared with thermosets, it is more environmentally friendly. It can be recycled and reused,  and has simple molding efficiency, lower cost etc. But its mechanical properties are worse than thermosets. Q. Using a long fiber reinforced thermoplastic material, will it block the die hole due to the long length of the fiber or not? A. ガラス長繊維やカーボン長繊維を使用する場合、LFT-Gに適しているかどうかを評価する必要があります。製品が小さすぎる場合、または塗布が長繊維材料に適していない場合。長繊維自体が金型ノズルに必要な要件を備えています。 Q. 長繊維強化熱可塑性材料を使用する場合、補強方法と材料の長さはどのように選択すればよいですか? A. 材料の選択は製品の要件によって異なります。製品の要求性能に応じて、内容物をどの程度強化するか、どの程度の長さが適切であるかを判断する必要があります。 アモイLFT複合プラスチック有限公司 ご提供させていただきます 1. LFTおよびLFRT材料の技術パラメータと最先端の設計 2. 金型正面の設計と推奨事項 3. 射出成形、押出成形等の技術サポートの提供

HDPE Introduction High-density polyethylene is an opaque white waxy material, lighter than water, specific gravity of 0.941 ~ 0.960, soft and tough, but slightly harder than LDPE, but also slightly elongated, non-toxic, odorless. Flammable, can continue to burn after leaving the fire, the upper end of the flame is yellow, the lower end is blue, will melt when burning, there are liquid drops, no black smoke, at the same time, emitting the smell of paraffin wax when burning. Acid and alkali resistance, organic solvent resistance, excellent electrical insulation, low temperature, can still maintain a certain degree of toughness. Surface hardness, tensile strength, rigidity and other mechanical strength are higher than LDPE, close to PP, tougher than PP, but the surface finish is not as good as PP. Poor mechanical properties, poor air permeability, easy to deformation, easy to aging, easy to brittle, brittle than PP, easy stress cracking, low surface hardness, easy to scratch. Difficult to print, when printing, surface discharge treatment is required, can not be plated, and the surface is not glossy. HDPE-Long glass fiber Because of its high crystallinity, poor impact strength and environmental cracking resistance and other defects, limiting its scope of application, so a lot of toughening modification HDPE research work has been carried out at home and abroad. Our company has greatly improved the performance of HDPE through the way of co-blending modification. Long fiber reinforced thermoplastic composites are reinforced thermoplastics with fiber lengths greater than 10mm. The reinforcing fibers are mainly glass fibers, carbon fibers, etc. Depending on the type of resin with appropriate fiber surface treatment, better results can be achieved. The addition of fiber material to the resin can greatly improve the overall material performance. Fiber composites absorb external forces in three ways: fiber pullout, fiber breakage, and resin fracture. The increase of fiber length consumes more energy for fiber pull-out, which is beneficial to the improvement of impact strength; the end of fiber in the composite is often the initiation point of crack growth, and the small number of long fiber ends also makes the impact strength increase; the long fiber blends entangle, flip and bend each other when filling the mold, unlike the short fiber blends which are arranged in the flow direction, therefore, the long fiber blends molded products are better than the same molded parts of short fiber blends. Therefore, compared with the same molded parts of short fiber blends, the long fiber blends have higher isotropy, better straightness, less warpage, and therefore better dimensional stability; the heat deflection temperature of long fiber reinforced thermoplastics is also increased than that of short fiber blends. Therefore, long-fiber composites exhibit better performance than short-fiber composites, which can improve rigidity, compression strength, bending strength, and creep resistance. プロセス ご参考までにTDS テスト 認証 品質マネジメントシステム ISO9001/16949認証取得 国立研究所認定証明書 変性プラスチック革新企業 名誉証明書 重金属のREACHおよびROSH試験 応用 お客様の製品イメージに基づいて技術サポートを提供いたします。 私たちに関しては 私たちはあなたに以下を提供します: 1. LFT & LFRT 材料技術パラメータと最先端の設計。 2. 金型のフロント設計と推奨事項。 3. 射出成形、押出成形などの技術サポートを提供します。 よくある質問 Q: 長繊維強化熱可塑性材料を使用する場合、補強方法と材料の長さをどのように選択すればよいですか? A: 材料の選択は製品の要件によって異なります。製品の要求性能に応じて、内容物をどの程度強化するか、どの程度の長さが適切であるかを判断する必要があります。 Q: 長繊維製品は射出成形に適しているだけでなく、押出成形などの加工も可能ですか? A: LFT 長ガラス繊維と長炭素繊維は主に射出成形に使用され、また、さまざまな熱可塑性プラスチック成形方法でプレート プロファイル チューブやモールド エッジを押出成形することもできます。 Q: 長繊維製品は原材料に比べてコストが高くなります。リサイクル価値は高いですか？ A: 熱可塑性 LFT 長繊維素材はリサイクルして再利用することができます。

PPA-LGF(ガラス長繊維) グレード：一般グレード 繊維仕様: 20%-60% 色: オリジナルの色 (カスタマイズ可能) 長さ：12mm程度（カスタマイズ可能） 特徴: 高靭性、低反り

PA12とは何ですか？ PA12 の学名はポリドデカラクタムで、ナイロン 12 としても知られています。その重合の基本原料はブタジエンであり、石油化学製品に依存する場合があります。これは半結晶質から結晶質の熱可塑性材料です。その特性は PA11 と似ていますが、結晶構造が異なります。PA12 は優れた電気絶縁体であり、他のポリアミドと同様に、湿気による絶縁特性の影響を受けません。PA12 は、多くの改善された可塑化特性と強化特性を備えています。 PA12-LGFとは何ですか? PA12充填長ガラス繊維材料は、元のナイロン12材料をベースに長ガラス繊維を加えた複合材料であり、材料に次の特性を持たせます：高温耐性、良好な寸法安定性、良好な靭性、良好な絶縁性、良好な耐食性 。 、高い機械的強度。 参考用のデータシート 応用 自動車、スポーツ部品、太陽エネルギー、太陽光発電産業、その他の産業に適しています。       詳細 番号 色 長さ サンプル MOQ パッケージ 積荷港 納期 PA12-NA-LGF30 ナチュラルカラー（またはカスタマイズ） 12mm程度（またはカスタム） 利用可能 25KG 25kg/袋 厦門港 発送後7-15日 私たちについて_ アモイ LFT 複合プラスチック有限公司は、LFT と LFRTに焦点を当てたブランド企業です  。ガラス長繊維シリーズ (LGF ) および炭素長繊維シリーズ (LCF )。同社の熱可塑性 LFT は、LFT-G 射出成形および押出成形に使用できるほか、LFT-D 成形にも使用できます。お客様のご要望に合わせて製作可能です: 長さ5~25mm。同社の長繊維連続浸透強化熱可塑性プラスチックは ISO9001&16949 システム認証に合格しており、製品は多くの国内商標と特許を取得しています。 さらに詳しい技術サポートが必要な場合は、お気軽にお問い合わせください。

PP-LGF 数ある複合材料の中でも、長尺ガラス強化ポリプロピレン材料（PP-LGF）は、低価格、優れた機械的特性、環境への優しさから人気が高まっています。ガラス短繊維強化ポリプロピレン材料（PP-SGF）と比較して、PP-LGFは強度、剛性、反り、耐疲労性、ノッチ衝撃強度、寸法安定性において優れているため、PP-LGFで製造された製品はさらなる重量とコストを実現できます。割引。 当社が製造するPP-LGF粒子の長さは一般的に8mm〜15mmで、ガラス繊維の含有量は20%〜60%に達し、粒子内のガラス繊維の保持長は1mm〜3mmに達します。ガラス繊維の残存長がわずか0.2mm～0.4mmのPP-SGF材に対し、PP-LGFは内部繊維の三次元網目構造により以下の特性を保証します。  1. 低密度: スチールの代わりに長ガラス繊維強化複合材料を使用することは、製品の重量を軽減する効果的な方法です。  2.高強度：変性樹脂と異なる長さの繊維を組み合わせた複合材料は、高い機械的強度、優れた剛性、衝撃性能を備えており、鋼板に代わるカバーや構造部品を製造できます。 3. 低コスト: 金属材料の代わりに長ガラス繊維強化複合材料を使用することで、複雑な金属部品の設計を簡素化し、複雑な部品を一度に形成するという目的を達成できます。 4.耐衝撃性：樹脂の弾性変形特性により、ガラス長繊維強化複合材料は衝突エネルギーを吸収する一定の機能を有し、一定の速度の衝撃に対して大きな緩衝効果を発揮します。 5.耐食性：複合材料は耐食性が強く、酸、アルカリ、塩に対する耐食性は金属よりも優れています。 6.美しさ：ほとんどの樹脂は着色性に優れており、マスターバッチを追加したり、表面に塗料をスプレーしたりすることでさまざまな色を作ることができます。射出成形により、さまざまな不規則な曲率形状を実現できます。 参考用のデータシート テスト 応用 PP-LGFは、最も注目されている素材として、自動車部品、洗濯機部品など、多くの分野でお客様にご利用いただいております。 ご連絡いただければ、技術サポートを提供いたします。 会社について アモイ LFT 複合プラスチック有限公司は、LFT と LFRTに焦点を当てたブランド企業です  。ガラス長繊維シリーズ (LGF ) および炭素長繊維シリーズ (LCF )。同社の熱可塑性 LFT は、LFT-G 射出成形および押出成形に使用できるほか、LFT-D 成形にも使用できます。お客様のご要望に合わせて製作可能です: 長さ5~25mm。同社の長繊維連続浸透強化熱可塑性プラスチックは ISO9001&16949 システム認証に合格しており、製品は多くの国内商標と特許を取得しています。

PBTプラスチック ポリブチレンテレフタレート (PBT) はポリエステル系に属し、1.4-pbt ブチレングリコール (1.4-ブチレングリコール) とテレフタル酸 (PTA) またはテレフタル酸エステル (DMT) の重縮合で作られ、分子式は (C8H8-C4H6) です。 -C3H3N)xを配合し、乳白色半透明〜不透明の結晶性熱可塑性ポリエステル樹脂を配合。PBT は最も丈夫なエンジニアリング熱可塑性プラスチックの 1 つであり、非常に優れた化学的安定性、機械的強度、電気絶縁特性、熱安定性を備えた半結晶材料です。 比重：1.31g/cm。 融点：225～275℃ ガラス転写温度（Tg）：22～43℃ ロックウェル硬度（Rスケール）：118 吸水率：0.34％ 成形収縮率：1.7～2.3％ PBT-LGF強化プラスチック 機械的性質に優れ、機械的強度、耐疲労性、寸法安定性に優れ、クリープも小さい。これらの特性は高温条件下でもほとんど変化しません。 PBT の製造では消費エネルギーが少なくなります。 耐熱性に優れ、強化後のUL温度指数は120～140℃であり、屋外での長期老化にも優れています。 耐溶剤性に優れ、ストレスクラックがありません。 PBTはUL94V-0レベルまでの難燃化が容易であり、難燃剤との親和性が良いため、反応性難燃グレードや付加難燃グレードの開発が容易です。難燃性製品は電気および電子産業で広く使用されています。 セレクトPBTは水分と接触すると分解しやすいため、高温多湿環境での使用には注意が必要です。 優れた電気特性、高い体積抵抗率と絶縁耐力、優れた耐アーク性、吸湿性が少なく、湿気や高温の環境下でも安定した電気特性を備えており、電子・電気部品に最適な材料です。 成形や二次加工が容易で、一般的な設備で射出成形や押出成形が可能です。結晶化速度が速く、流動性が良いため、他のエンジニアリング材料に比べて金型温度が低く、薄肉部品の加工にかかる時間はわずか数秒、大型部品の加工時間はわずか40～60秒です。 参考用のデータシート 応用 1、電子機器: ヒューズレスワイヤーブレーカー、電磁開閉器、変圧器、家電ハンドル、コネクタ、シェルなど 2、 自動車: ドアハンドル、バンパー、ディストリビューターカバー、フェンダー、ワイヤーガードシェル、ホイールカバーなど 3 、産業用部品：OAファン、キーボード、リール、部品、ランプシェードなど 製品加工 射出成形 詳細 番号 色 長さ サンプル MOQ パッケージ 積荷港 納期 PBT-NA-LGF30 ナチュラルカラー（カスタマイズ可能） 12mm (カスタマイズ可能) 利用可能 1トン 25kg/袋 厦門港 発送後7-15日 研究所と工場 よくある質問 Q. 長ガラス繊維と長炭素繊維の射出成形には、射出成形機や金型に特別な要件がありますか? A. 確かに要件はあります。特に製品設計構造、射出成形機のスクリューノズル、金型構造から、射出成形プロセスでは長繊維の要件を考慮する必要があります。 Q. 長いガラス繊維で強化した後、射出成形の際にプラスチック製品の表面にガラス繊維が入り込み、製品の表面が荒れて繊維が浮いてしまうことがあります。材料の表面を滑らかにするにはどうすればよいでしょうか？ A. 射出成形プロセスでは、プラスチック粒子が十分に可塑化および分散されていることを確認する必要があります。また、プラスチック粒子の乾燥時に水分が除去されていないことを確認し、金型温度を適切な温度に調整し、金型表面を所定の位置で研磨する必要があります。

ポリアミド 6 プラスチック ナイロン 6 (PA6) は、ポリアミド 6、ナイロン 6 とも呼ばれ、機械的強度と結晶性が良好で、耐食性、耐摩耗性などの特性があり、自動車産業、鉄道輸送、フィルム包装、電子機器、繊維製品などに使用されています。その他の主要分野でも幅広い応用が可能です。 PA6は総合的な性能を備えていますが、強酸や強アルカリに対する耐性があまり強くなく、低温、乾燥状態での衝撃強度が高くない、親水基の存在により吸水率が高くなる、などの一連の欠点もあります。弾性率、耐クリープ性、衝撃強度、その他の吸水性が大幅に低下するため、製品の寸法安定性に影響を与えるだけでなく、製品の電気特性にも影響します。 したがって、PA6 の修正については十分な研究を行う必要があります。 ポリアミド6充填長炭素繊維 炭素繊維強化複合材料は、高強度繊維と弾性プラスチックからなる複合材料であり、剛性と強度が高く、耐熱性、耐衝撃性、寸法安定性に優れ、産業用や生活用としての要求に応えます。 PA6-LCFは従来のポリアミドよりも剛性と強度が高く、炭素繊維を添加することで材料の熱安定性が増し、耐摩耗性が向上し、高強度、高耐衝撃性、熱変形耐性を備えた複合材料です。 参考のためのTDS 応用分野 研究所と工場 私たちはあなたに提供することができます LFT & LFRT 材料の技術パラメータと最先端の設計 金型前面の設計と推奨事項 射出成形、押出成形などの技術サポートを提供します。